Description
Due to supply chain challenges the cartridge on this product is being changed. The new 415ml cartridge (3032005) replaces the original 375ml cartridge (3019922). This cartridge requires different guns and mixing tips compared to the old packaging. Please contact us with any questions regarding this change.
Lord Maxlok MX/T3, MX/T6 and MX/T18 acrylic adhesives replace welding, brazing, riveting and other mechanical fastening methods especially over a wide range of temperature environments subject to high impact or high peel loads. LORD Maxlok acrylic adhesives are available in a range of working times to accommodate a wide variety of process requirements.
Features and Benefits:
- Versatile – bonds a wide range of unprepared metals with minimal substrate preparation.
- Temperature Resistant – performs at temperatures from -40 to +300°F (-40 to +149°C).
- Environmentally Resistant – resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray and weathering; provides excellent resistance to indirect UV exposure.
- UL Rated – Maxlok MX/T6 adhesive system is UL 746C certified.
- Precise Bondline – allows precise control of adhesive bondline thickness due to its content of glass beads, 0.01″ (0.025 cm) diameter.
- Non-Sag – remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility
| MX Accelerator | T3 Adhesive | T6 Adhesive | T18 Adhesive | |
| Appearance | Grey Paste | Off-white to Tan Paste | Off-white to Tan Paste | Off-white to Tan Paste |
| Viscosity | 170,000-320,000 | 70,000-120,000 | 80,000-180,000 | 80,000-180,000 |
| Density
lb/gal (kg/m^3) |
11.5-12.1
(1378-1450) |
8.3-8.7
(995-1042) |
8.4-8.9
(1007-1066) |
8.4-8.9
(1007-1066) |
| Flash Point, °F (°C) | 201 (94) | 59 (15) | 59 (15) | 59 (15) |
| MX/T3 | MX/T6 | MX/T18 | |
| Mix Ratio by Volume, Accelerator to Adhesive | 1:4 | 1:4 | 1:4 |
| Solids Content, % | 100 | 100 | 100 |
| Working Time, min @ 77°F (25°C) | 3-5 | 6-9 | 18-24 |
| Time to Handling Strength, min @ 77°F (25°C) | 6-8 | 20-24 | 48-72 |
| Mixed Appearance | Grey Paste | Grey Paste | Grey Paste |
| Tensile Strength at Break, psi (MPa) | 2800 (19.3) |
| Elongation, % | >10 |
| Young’s Modulus, psi (MPa) | 108,778 (750) |
| Glass Transition Temperature, °F(°C) | 194 (90) |
| Substrates | Aluminum to Aluminum | HDG to HDG | EZG to EZG |
| Lap Shear @ Room Temperature, psi (MPa)
Failure Mode |
2760 (19)
Cohesive |
2410 (16.6)
Cohesive |
2190 (15.1)
Cohesive |
| Lap Shear @ Hot Strength [180°F (82°C)], psi (MPa)
Failure Mode |
1030 (7.1)
Cohesive |
1150 (7.9)
Cohesive |
1000 (6.9)
Cohesive |
| Lap Shear after 1400 hours Salt Spray
Exposure, psi (MPa) Failure Mode |
2140 (14.8)
Cohesive |
1760 (12.1)
Cohesive |
1430 (9.9)
Cohesive |
| Lap Shear @ -40°F (-40°C), psi (MPa)
Failure Mode |
3150 (21.7)
Cohesive/Adhesive |
2400 (16.5)
Cohesive/Adhesive |
2550 (17.6)
Cohesive |
| T-Peel, pli (N/mm)
Failure Mode |
41 (7.2)
Cohesive |
53 (9.3)
Cohesive |
54 (9.5)
Cohesive |
| Substrates | ABS to ABS | FRP to FRP |
| Lap Shear @ Room Temperature, psi (MPa)
Failure Mode |
520 (3.6)
Stock Break |
1280 (8.8)
Fiber Tear |
| Lap Shear after 1400 hours Salt Spray
Exposure, psi (MPa) Failure Mode |
460 (3.2)
Stock Break |
520 (3.6)
Fiber Tear |
| Lap Shear @ -40°F (-40°C), psi (MPa)
Failure Mode |
920 (6.3)
Stock Break |
869 (5.99)
Fiber Tear |
| Pak-50 | 300mL x 75mL Cartridge |
 Chem-Set™ PAK-50 Gun |
 Newborn 535XSP Professional Gun |
 TAH 190-620 Static Mixer |
 Chem-Set™ MCQ 08-24T Mixing Tip |