Description
Looking for a strong, versatile adhesive that can replace welding, brazing, and riveting? Look no further than LORD Maxlok MX/T18 acrylic adhesive. This high-performance adhesive is designed for bonding a wide range of unprepared metals and plastics, and it offers excellent resistance to temperature, environmental factors, and harsh chemicals.
Key Features:
- Versatile: Bonds a wide range of metals and plastics with minimal surface preparation.
- Temperature Resistant: Performs at temperatures from -40°F to +300°F (-40°C to +149°C).
- Environmentally Resistant: Resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray, and weathering.
- Long Working Time: 18-24 minutes at 77°F (25°C) allows for greater process flexibility.
- Non-Sag: Remains in position when applied on vertical or overhead surfaces.
- Precise Bondline: Glass beads ensure a controlled bondline thickness of 0.01″ (0.25 cm).
Ideal for:
- Automotive assembly
- Appliance manufacturing
- HVAC equipment
- Metal fabrication
- Transportation applications
- And many more!
Packaging Update:
Due to supply chain challenges the cartridge on this product is being changed. The new 415ml cartridge (3032005) replaces the original 375ml cartridge (3019922). This cartridge requires different guns and mixing tips compared to the old packaging. Please contact us with any questions regarding this change.
| MX/T3 | MX/T6 | MX/T18 | |
| Mix Ratio by Volume, Accelerator to Adhesive | 1:4 | 1:4 | 1:4 |
| Solids Content, % | 100 | 100 | 100 |
| Working Time, min @ 77°F (25°C) | 3-5 | 6-9 | 18-24 |
| Time to Handling Strength, min @ 77°F (25°C) | 6-8 | 20-24 | 48-72 |
| Mixed Appearance | Grey Paste | Grey Paste | Grey Paste |
| Tensile Strength at Break, psi (MPa) | 2800 (19.3) |
| Elongation, % | >10 |
| Young’s Modulus, psi (MPa) | 108,778 (750) |
| Glass Transition Temperature, °F(°C) | 194 (90) |
| Substrates | Aluminum to Aluminum | HDG to HDG | EZG to EZG |
| Lap Shear @ Room Temperature, psi (MPa)
Failure Mode |
2760 (19)
Cohesive |
2410 (16.6)
Cohesive |
2190 (15.1)
Cohesive |
| Lap Shear @ Hot Strength [180°F (82°C)], psi (MPa)
Failure Mode |
1030 (7.1)
Cohesive |
1150 (7.9)
Cohesive |
1000 (6.9)
Cohesive |
| Lap Shear after 1400 hours Salt Spray
Exposure, psi (MPa) Failure Mode |
2140 (14.8)
Cohesive |
1760 (12.1)
Cohesive |
1430 (9.9)
Cohesive |
| Lap Shear @ -40°F (-40°C), psi (MPa)
Failure Mode |
3150 (21.7)
Cohesive/Adhesive |
2400 (16.5)
Cohesive/Adhesive |
2550 (17.6)
Cohesive |
| T-Peel, pli (N/mm)
Failure Mode |
41 (7.2)
Cohesive |
53 (9.3)
Cohesive |
54 (9.5)
Cohesive |
| Substrates | ABS to ABS | FRP to FRP |
| Lap Shear @ Room Temperature, psi (MPa)
Failure Mode |
520 (3.6)
Stock Break |
1280 (8.8)
Fiber Tear |
| Lap Shear after 1400 hours Salt Spray
Exposure, psi (MPa) Failure Mode |
460 (3.2)
Stock Break |
520 (3.6)
Fiber Tear |
| Lap Shear @ -40°F (-40°C), psi (MPa)
Failure Mode |
920 (6.3)
Stock Break |
869 (5.99)
Fiber Tear |
Order your LORD Maxlok MX/T18 acrylic adhesive today and experience the difference!