LORD Maxlok MX/T6 (4:1) Acrylic Adhesive – 375 ml Cartridge – Being Discontinued Due to Cartridge Change

SKU: LOR3019621

Call for pricing and availability
You save

  • Expert Support

  • 50+ Years of Experience

  • Same Day Shipping*

*On in-stock items, placed by 2pm EST

Ask An Expert

Our engineers are ready to help!

Get In Touch Now

Description

Due to supply chain challenges the cartridge on this product is being changed. A new 415ml cartridge (3032002) replaces this original 375ml cartridge (3019621). This cartridge requires different guns and mixing tips compared to the old packaging. Please contact us with any questions regarding this change.

Lord Maxlok MX/T3, MX/T6 and MX/T18 acrylic adhesives replace welding, brazing, riveting and other mechanical fastening methods, especially over a wide range of temperature environments subject to high impact or high peel loads. LORD Maxlok acrylic adhesives are available in a range of working times to accommodate a wide variety of process requirements.

Features and Benefits:

  • Versatile – bonds a wide range of unprepared metals with minimal substrate preparation. 
  • Temperature Resistant – performs at temperatures from -40 to +300°F (-40 to +149°C). 
  • Environmentally Resistant – resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray and weathering; provides excellent resistance to indirect UV exposure. 
  • UL Rated – Maxlok MX/T6 adhesive system is UL 746C certified. 
  • Precise Bondline – allows precise control of adhesive bondline thickness due to its content of glass beads, 0.01″ (0.025 cm) diameter. 
  • Non-Sag – remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility
Typical Properties
  MX Accelerator T3 Adhesive T6 Adhesive T18 Adhesive
Appearance Grey Paste Off-white to Tan Paste Off-white to Tan Paste Off-white to Tan Paste
Viscosity 170,000-320,000 70,000-120,000 80,000-180,000 80,000-180,000
Density

lb/gal

(kg/m^3)

11.5-12.1

(1378-1450)

8.3-8.7

(995-1042)

8.4-8.9

(1007-1066)

8.4-8.9

(1007-1066)

Flash Point, °F (°C)  201 (94) 59 (15) 59 (15) 59 (15)
 
Typical Properties Of Adhesive Mixed with Accelerator
  MX/T3 MX/T6 MX/T18
Mix Ratio by Volume, Accelerator to Adhesive 1:4 1:4 1:4
Solids Content, % 100 100 100
Working Time, min @ 77°F (25°C) 3-5 6-9 18-24
Time to Handling Strength, min @ 77°F (25°C) 6-8 20-24 48-72
Mixed Appearance Grey Paste Grey Paste Grey Paste
 
Typical Cured Properties
Tensile Strength at Break, psi (MPa) 2800 (19.3)
Elongation, % >10
Young’s Modulus, psi (MPa) 108,778 (750)
Glass Transition Temperature, °F(°C) 194 (90)
 
Metal Bond Performance
Substrates Aluminum to Aluminum HDG to HDG EZG to EZG
Lap Shear @ Room Temperature, psi (MPa)

Failure Mode

2760 (19)

Cohesive

2410 (16.6)

Cohesive

2190 (15.1)

Cohesive

Lap Shear @ Hot Strength [180°F (82°C)], psi (MPa)

Failure Mode

1030 (7.1)

Cohesive

1150 (7.9)

Cohesive

1000 (6.9)

Cohesive

Lap Shear after 1400 hours Salt Spray

Exposure, psi (MPa)

Failure Mode

2140 (14.8)

Cohesive

1760 (12.1)

Cohesive

1430 (9.9)

Cohesive

Lap Shear @ -40°F (-40°C), psi (MPa)

Failure Mode

3150 (21.7)

Cohesive/Adhesive

2400 (16.5)

Cohesive/Adhesive

2550 (17.6)

Cohesive

T-Peel, pli (N/mm)

Failure Mode

41 (7.2)

Cohesive

53 (9.3)

Cohesive

54 (9.5)

Cohesive

 
Plastic/Composite Bond Performance
Substrates ABS to ABS FRP to FRP
Lap Shear @ Room Temperature, psi (MPa)

Failure Mode

520 (3.6)

Stock Break

1280 (8.8)

Fiber Tear

Lap Shear after 1400 hours Salt Spray

Exposure, psi (MPa)

Failure Mode

460 (3.2)

Stock Break

520 (3.6)

Fiber Tear

Lap Shear @ -40°F (-40°C), psi (MPa)

Failure Mode

920 (6.3)

Stock Break

869 (5.99)

Fiber Tear

Additional information

Weight 1.3 lbs
Dimensions 3 × 2 × 10.00 in
Product Restrictions

Manufacturer

Component

Ratio

Gun Size

Packaging Size General

Packaging Size Specific

Type

Must Ship Freight

Country Of Manufacture

Origin

Reviews

There are no reviews yet.

Be the first to review “LORD Maxlok MX/T6 (4:1) Acrylic Adhesive – 375 ml Cartridge – Being Discontinued Due to Cartridge Change”

Your email address will not be published. Required fields are marked *

You may also like…